Aluminum Scandium Nitride Films: Enabling Next-Gen Ferroelectric Memory Devices These films' high stability and superior ferroelectric properties at high-temperature H2-included heat treatment make them promising for next-generation ferroelectric memory devices.

Aluminum scandium nitride thin films could pave the way for the next generation of ferroelectric memory devices, according to a new study from Tokyo Tech. Compared to existing ferroelectric materials, these films maintain their ferroelectric properties and crystal structure even after heat treatment at temperatures up to 600 °C in both hydrogen and argon atmospheres. This high stability makes them ideal for high-temperature manufacturing processes under the H₂-included atmosphere used in fabricating advanced memory devices.

Imagine a thin film, just nanometers thick, that could store gigabytes of data – enough for movies, video games, and videos. This is the exciting potential of ferroelectric materials for memory storage. These materials have a unique arrangement of ions, resulting in two distinct polarization states analogous to 0 and 1 in binary code, which can be used for digital memory storage. These states are stable, meaning they can 'remember' data without power, and can be switched efficiently by applying a small electric field. This property makes them extremely energy-efficient and capable of fast read and write speeds. However, some well-known ferroelectric materials, such as Pb(Zr,Ti)O₃ (PZT) and SrBi₂Ta₂O₉, degrade and lose their polarization when exposed to heat treatment with hydrogen during fabrication.

In a study published in the journal Applied Physics Letters, a research team led by Assistant Professor Kazuki Okamoto and Hiroshi Funakubo at Tokyo Institute of Technology (Tokyo Tech), in collaboration with Canon ANELVA Corporation and Japan Synchrotron Radiation Research Institute (JASRI), has shown that aluminum scandium nitride (AlScN) ferroelectric films remain stable and maintain their ferroelectric properties at temperatures up to 600°C.

"Our results attest to the high stability of the ferroelectricity of the films subjected to heat treatment in hydrogen-included atmosphere, regardless of the electrode material. This is a highly promising result for next-generation ferroelectric memory devices and offers more processing options," says Funakubo.

For ferroelectric materials to be compatible with high-temperature fabrication processes under an H₂-included atmosphere, they ideally should experience little to no degradation in their crystal structure and ferroelectric properties. Two crucial parameters in this regard are remnant polarization (P_r) and coercive field (E_c). P_r refers to the polarization retained after removing the electric field, while Ec is the electric field required to switch the material's polarization state. AlScN has a higher P_r (>100 µC/cm²) than PZT (30–50 µC/cm²). However, the impact of heat treatment under an H₂-included atmosphere on its properties was unclear until now.

To investigate this, the researchers deposited (Al_0.8Sc_0.2)N film on a silicon substrate using sputtering at 400°C. The films were placed between two electrodes of platinum (Pt) and titanium nitride (TiN). Electrodes play a crucial role in the material's stability. Pt encourages the incorporation of hydrogen gas into the film, while TiN acts as a barrier to H₂ diffusion. So, evaluating its performance with different electrode materials is crucial.

The films underwent post-heat-treatment in a hydrogen and argon atmosphere for 30 minutes at temperatures ranging from 400 to 600 °C at 800 Torr. The researchers used X-ray diffraction (XRD) to examine changes in the crystal structure in the bulk and the film-electrode interface. Positive-up-negative-down (PUND) measurements were used to evaluate P_r and E_c. This technique involves applying positive and negative electric fields to the film and observing the resulting polarization response.

The films maintained a stable wurtzite-type crystal structure. P_r remained stable above 120 µC/cm², regardless of the electrode or treatment atmosphere, a value five times larger than HfO₂-based films and three times larger than that of PZT. Furthermore, E_c increased only slightly by about 9%. This increase was attributed to changes in the film's crystal lattice constant not due to the presence of hydrogen or the choice of electrode used. Notably, unlike other ferroelectric materials susceptible to hydrogen diffusion, the high bond energy between Al and N prevents hydrogen from penetrating the film.

"The results show that (Al_0.8Sc_0.2)N is much more resistant to degradation by post-heat treatment than conventional ferroelectric and HfO₂-based ferroelectric films," says Funakubo. With a relatively stable crystal structure, a high P_r value, and a small change in E_c, (Al,Sc)N films are a promising candidate for next-generation ferroelectric memory devices.